ULTRASTRONG, STIFF AND MULTIFUNCTIONAL CARBON NANOTUBE COMPOSITES

"Ultrastrong, Stiff and Multifunctional Carbon Nanotube Composites". X. Wang, Z. Z. Yong, Q. W. Li, P. D. Bradford, W. Liu, D. S. Tucker, W. Cai, H. Wang, F. G. Yuan, Y. T. Zhu. MATERIALS RESEARCH LETTERS In press. DOI: 10.1080/21663831.2012.686586

Carbon nanotubes (CNTs) are an order of magnitude stronger than any other current engineering fiber. However, for the past two decades, it has been a challenge to utilize their reinforcement potential in composites. Here, we report CNT composites with unprecedented multifunctionalities, including record high strength (3.8 GPa), high Young's modulus (293 GPa), electrical conductivity (1230 S·cm ⁻¹), and thermal conductivity (41 W m ⁻¹ K ⁻¹). These superior properties are derived from the long length, high volume fraction, good alignment and reduced waviness of the CNTs, which were produced by a novel-processing approach that can be easily scaled up for industrial production.

Los nanotubos de carbono (CNTs) son un orden de magnitud más resistentes que cualquier otra fibra actual. Sin embargo, durante las últimas dos décadas, ha resultado ser todo un reto utilizarlos para reforzar compositos. Aquí se reportan compositos de CNT con multifuncionalidades sin precedentes, incluyendo una alta resistencia récord (3.8 GPa), un alto módulo de Young (293 GPa), una alta conductividad eléctrica (1230 S·cm ⁻¹), y una alta conductividad térmica (41 W m ⁻¹ K ⁻¹). Estas propiedades superiores provienen de la gran longitud, alta fracción de llenado, buena alineación y ondulación reducida de los CNTs, los cuales se producen por una novedosa estrategia de procesado que puede escalarse fácilmente para su producción industrial.

http://www.tandfonline.com/doi/abs/10.1080/21663831.2012.686586